Transparent, near infrared-shielding glass ceramic

ABSTRACT

Optically transparent glass ceramic materials comprising a glass phase containing and a crystalline tungsten bronze phase comprising nanoparticles and having the formula M x WO 3 , where M includes at least one H, Li, Na, K, Rb, Cs, Ca, Sr, Ba, Zn, Cu, Ag, Sn, Cd, In, Tl, Pb, Bi, Th, La, Pr, Nd, Sm, Eu, Gd, Dy, Ho, Er, Tm, Yb, Lu, and U, and where 0&lt;x&lt;1. Aluminosilicate and zinc-bismuth-borate glasses comprising at least one of Sm 2 O 3 , Pr 2 O 3 , and Er 2 O 3  are also provided.

This application claims the benefit of priority under 35 U.S.C. §119 of U.S. Provisional Application Ser. No. 61/352,602 filed on Jun. 21, 2016, which claims the benefit of priority under 35 U.S.C.§119 of U.S. Provisional Application Ser. No. 62/351,616 filed on Jun. 17, 2016, the content of which is relied upon and incorporated herein by reference in its entirety.

BACKGROUND

The disclosure relates to glass ceramic materials. More particularly, the disclosure relates to optically transparent glass ceramic materials. Even more particularly, the disclosure relates to optically transparent glass ceramic materials having a crystalline tungsten bronze phase.

Near infrared (NIR)-shielding glasses are being developed to block and/or eliminate wavelengths ranging from 700-2500 nm for applications ranging from optical filters, lenses, and glazing for medical, defense, aerospace, and consumer applications.

Low emittance (low-E) coatings have been developed to minimize the amount of ultraviolet and infrared light that can pass through glass without compromising the amount of visible light that is transmitted. Low-E coatings are typically either sputtered or pyrolytic coatings. Alternatively, low-E plastic laminates may be retrofitted to a glass substrate.

Thin films, coatings, and composite materials containing nano- or micron-sized particles of non-stoichiometric tungsten suboxides or doped non-stoichiometric tungsten trioxides (referred to as tungsten bronzes) have been used to provide near infrared shielding with high transparency in the visible spectrum. However, tungsten bronze films often require expensive vacuum deposition chambers, have limited mechanical robustness, and are susceptible to oxygen, moisture, and UV light, all of which cause the NIR shielding performance of these materials to decrease and to discolor and degrade transparency in the visible light range.

SUMMARY

The present disclosure provides optically transparent glass ceramic materials which, in some embodiments, comprise a glass phase containing at least about 80% silica by weight and a crystalline tungsten bronze phase having the formula M_(x)WO₃, where M includes, but is not limited to, at least one of H, Li, Na, K, Rb, Cs, Ca, Sr, Ba, Zn, Cu, Ag, Sn, Cd, In, Tl, Pb, Bi, Th, La, Pr, Nd, Sm, Eu, Gd, Dy, Ho, Er, Tm, Yb, Lu, and U, and where 0<x<1. The crystalline tungsten bronze phase comprises nanoparticles. The glass ceramic, in some embodiments, has a low coefficient of thermal expansion (CTE), strong attenuation or blocking of ultraviolet (UV) radiation at wavelengths of less than about 360 nm and near infrared (NIR) radiation at wavelengths ranging from about 700 nm to about 3000 nm. Aluminosilicate and zinc-bismuth-borate glasses comprising at least one of Sm₂O₃, Pr₂O₃, and Er₂O₃ are also provided.

Accordingly, one aspect of the disclosure is to provide a glass ceramic comprising a silicate glass phase and from about 1 mol % to about 10 mol % of a crystalline M_(x)WO₃ phase comprising nanoparticles, where M is at least one of H, Li, Na, K, Rb, Cs, Ca, Sr, Ba, Zn, Cu, Ag, Sn, Cd, In, Tl, Pb, Bi, Th, La, Pr, Nd, Sm, Eu, Gd, Dy, Ho, Er, Tm, Yb, Lu, and U, and where 0<x<1.

A second aspect of the disclosure is to provide a glass ceramic comprising a silicate glass phase and from about 1 mol % to about 10 mol % of a crystalline M_(x)WO₃ phase comprising nanoparticles, where M is at least one alkali metal, and 0<x<1.

In another aspect an aluminosilicate glass comprising SiO₂, Al₂O₃, and at least one of Sm₂O₃, Pr₂O₃, and Er₂O₃, where Sm₂O₃+Pr₂O₃+Er₂O₃≦30 mol %, is also provided. The aluminosilicate glass, in some embodiments, comprises from about 8 mol % to about 45 mol % Al₂O₃, from about 40 mol % to about 72 mol % SiO₂ and at least one of Sm₂O₃, Pr₂O₃, and Er₂O₃, wherein Sm₂O₃+Pr₂O₃+Er₂O₃≦30 mol %. In some embodiments, the aluminosilicate glass further comprises at least one alkaline earth oxide and B₂O₃. The glasses, in some embodiments, have less than about 30% transmission at a wavelength between about 1400 nm and about 1600 nm.

In yet another aspect, a zinc-bismuth-borate glass comprising ZnO, Bi₂O₃, B₂O₃, and at least one of Sm₂O₃, Pr₂O₃, and Er₂O₃, where Sm₂O₃+Pr₂O₃+Er₂O₃≦12 mol %. In some embodiments, the Zn—Bi-borate glasses further comprise at least one of Na₂O and TeO₂. These glasses, in some embodiments, have less than about 30% transmission at a wavelength between about 1400 nm and about 1600 nm.

In another aspect, a phosphate glass comprising at least one rare earth oxide Ln₂O₃ and having a molar ratio 25Ln₂O₃:75P₂O₅, where Ln₂O₃ comprises at least one of Sm₂O₃, Pr₂O₃, and Er₂O₃ is provided. In some embodiments the phosphate glass comprises: from about 6 mol % to about 25% Ln₂O₃; from about 5 mol % to about 27% Al₂O₃; and from about 67 mol % to about 74 mol % P₂O₅.

These and other aspects, advantages, and salient features will become apparent from the following detailed description, the accompanying drawings, and the appended claims.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a plot of absorbance vs. wavelength of splat-quenched, annealed, and heat-treated glass ceramic samples;

FIG. 2 is a plot of spectra of splat-quenched (A), annealed (B), and heat-treated (C) glass ceramic compositions;

FIG. 3 is a plot of differential scanning calorimetry cooling curves measured for glass ceramic samples;

FIG. 4 is a plot of spectra of glass ceramics containing different alkali tungsten bronzes;

FIG. 5 is an x-ray powder diffraction profile of a splat-quenched glass ceramic;

FIG. 6 is an x-ray powder diffraction profile of a heat-treated glass ceramic;

FIG. 7 is a flow chart for a method of infiltrating a glass to form a glass ceramic;

FIG. 8 is a plot of a dispersion curve for glass E listed in Table E;

FIG. 9 is a plot of transmission for glass E listed in Table E; and

FIG. 10 is a plot of transmission for glasses J, K, and L listed in Table F.

DETAILED DESCRIPTION

In the following description, like reference characters designate like or corresponding parts throughout the several views shown in the figures. It is also understood that, unless otherwise specified, terms such as “top,” “bottom,” “outward,” “inward,” and the like are words of convenience and are not to be construed as limiting terms. In addition, whenever a group is described as comprising at least one of a group of elements and combinations thereof, it is understood that the group may comprise, consist essentially of, or consist of any number of those elements recited, either individually or in combination with each other. Similarly, whenever a group is described as consisting of at least one of a group of elements or combinations thereof, it is understood that the group may consist of any number of those elements recited, either individually or in combination with each other. Unless otherwise specified, a range of values, when recited, includes both the upper and lower limits of the range as well as any ranges therebetween. As used herein, the indefinite articles “a,” “an,” and the corresponding definite article “the” mean “at least one” or “one or more,” unless otherwise specified. It also is understood that the various features disclosed in the specification and the drawings can be used in any and all combinations.

As used herein, the terms “glass article” and “glass articles” are used in their broadest sense to include any object made wholly or partly of glass and/or glass ceramics, and includes laminates of the glasses and glass ceramics described herein with conventional glasses. Unless otherwise specified, all compositions are expressed in terms of mole percent (mol %). Coefficients of thermal expansion (CTE) are expressed in terms of 10⁻⁷/° C. and represent a value measured over a temperature range from about 20° C. to about 300° C., unless otherwise specified.

As used herein, the terms “nanoparticle” and “nanoparticles” refer to particles between about 1 and about 1,000 nanometers (nm) in size. As used herein, the terms “platelet” and “platelets” refer to flat or planar crystals. As used herein, the terms “nanorod” and “nanorods” refer to elongated crystals having a length of up to about 1,000 nm and an aspect ratio (length/width) of at least 3 and in some embodiments, in a range from about 3 to about 5.

As used herein, “transmission” and “transmittance” refer to external transmission or transmittance, which takes absorption, scattering and reflection into consideration. Fresnel reflection is not subtracted out of the transmission and transmittance values reported herein.

It is noted that the terms “substantially” and “about” may be utilized herein to represent the inherent degree of uncertainty that may be attributed to any quantitative comparison, value, measurement, or other representation. These terms are also utilized herein to represent the degree by which a quantitative representation may vary from a stated reference without resulting in a change in the basic function of the subject matter at issue. Thus, a glass that is “free of MgO” is one in which MgO is not actively added or batched into the glass, but may be present in very small amounts (e.g., less than 400 parts per million (ppm), or less than 300 ppm) as a contaminant.

Compressive stress and depth of layer are measured using those means known in the art. Such means include, but are not limited to, measurement of surface stress (FSM) using commercially available instruments such as the FSM-6000, manufactured by Orihara Co., Ltd. (Tokyo, Japan). Surface stress measurements rely upon the accurate measurement of the stress optical coefficient (SOC), which is related to the birefringence of the glass. SOC in turn is measured according to a modified version (hereinafter “the modification”) of Procedure C, which is described in ASTM standard C770-98 (2013), entitled “Standard Test Method for Measurement of Glass Stress-Optical Coefficient,” the contents of which are incorporated herein by reference in their entirety. The modification of Procedure C includes using a glass disc as the specimen having a thickness of 5 to 10 mm and a diameter of 12.7 mm. The disc is isotropic and homogeneous, and is core-drilled with both faces polished and parallel. The modification also includes calculating the maximum force, Fmax to be applied to the disc. The force should be sufficient to produce at least 20 MPa compression stress. Fmax is calculated using the equation:

Fmax=7.854·D·h

where: Fmax is maximum force, expressed in Newtons; D is the diameter of the disc, expressed in millimeters (mm); and h is the thickness of the light path, also expressed in mm. For each force applied, the stress is computed using the equation:

σ (MPa)=8F/(π·D·h)

where: F is the force, expressed in Newtons; D is the diameter of the disc, expressed in millimeters (mm); and h is the thickness of the light path, also expressed in millimeters.

Unless otherwise specified, the terms “depth of layer,” “DOL,” and “FSM_DOL” refer to the depth of the compressive layer as determined by surface stress measurements (FSM) measurements using commercially available instruments such as, but not limited to, the FSM-6000 stress meter. The depth of compression DOC refers to the depth at which the stress is effectively zero inside the glass and can be determined from the stress profile obtained using the refractive near field (RNF) and polarimetric methods that are known in the art. This DOC is typically less than the FSM_DOL measured by the FSM instrument for a single ion exchange process.

For strengthened glass articles in which the compressive stress layers extend to deeper depths within the glass, the FSM technique may suffer from contrast issues that affect the observed DOL value. At deeper depths of compressive layer, there may be inadequate contrast between the TE and TM spectra, thus making the calculation of the difference between the spectra of bound optical modes for TM and TE polarization—and accurate determination the DOL—more difficult. Moreover, the FSM software analysis is incapable of determining the compressive stress profile (i.e., the variation of compressive stress as a function of depth within the glass). In addition, the FSM technique is incapable of determining the depth of layer resulting from the ion exchange of certain elements in the glass such as, for example, the ion exchange of sodium for lithium.

The DOL as determined by the FSM is a relatively good approximation for the depth of the compressive layer of depth compression (DOC) when the DOL is a small fraction r of the thickness t and the index profile has a depth distribution that is reasonably well approximated with a simple linear truncated profile. When the DOL is a substantial fraction of the thickness, such as when DOL≧0.1·t, then the DOC is most often noticeably lower than the DOL. For example, in the idealized case of a linear truncated profile, the relationship DOC=DOL·(1−r) holds, where r=DOL/t.

Alternatively, the compressive stress, stress profile, and depth of layer may be determined using scattered linear polariscope (SCALP) techniques that are known in the art. The SCALP technique enables non-destructive measurement of surface stress and depth of layer.

Referring to the drawings in general and to FIG. 1 in particular, it will be understood that the illustrations are for the purpose of describing particular embodiments and are not intended to limit the disclosure or appended claims thereto. The drawings are not necessarily to scale, and certain features and certain views of the drawings may be shown exaggerated in scale or in schematic in the interest of clarity and conciseness.

Described herein are optically transparent glass ceramic materials which, in some embodiments, comprise a glass phase containing at least about 90% silica by weight and a crystalline tungsten bronze phase. These glass ceramics comprise a silicate glass phase and from about 0.1 mol % to about 10 mol %, or from about 1 mol % to about 4 mol %, or from about 0.5 mol % to about 5 mol % of a crystalline tungsten bronze phase comprising crystalline M_(x)WO₃ nanoparticles. In one embodiment, the crystalline M_(x)WO₃ nanoparticles are encapsulated within and dispersed within and, in some embodiments, throughout the residual glass phase. In another embodiment, the M_(x)WO₃ crystalline nanoparticles are disposed at or near the surface of the glass ceramic. In some embodiments, the M_(x)WO₃ crystalline nanoparticles are platelet-shaped and have an average diameter, determined by those means known in the art (e.g., SEM and/or TEM microscopy, x-ray diffraction, light scattering, centrifugal methods, etc.) ranging from about 10 nm to 1000 nm, or from about 10 nm to about 5 m, and/or M_(x)WO₃ nanorods having a high aspect ratio and an average length, determined by those means known in the art, ranging from 10 nm to 1000 nm, and an average width, determined by those means known in the art, ranging from about 2 to about 75 nm. In some embodiments, tungsten bronze glass ceramics that exhibit high visible transparency and strong UV and NIR absorption contain high aspect ratio (length/width) M_(x)WO₃ rods having an average length ranging from about 10 nm to about 200 nm and an average width ranging from about 2 nm to 30 nm. The crystalline tungsten bronze phase has the formula M_(x)WO₃, where M is at least one of H, Li, Na, K, Rb, Cs, Ca, Sr, Ba, Zn, Cu, Ag, Sn, Cd, In, Tl, Pb, Bi, Th, La, Pr, Nd, Sm, Eu, Gd, Dy, Ho, Er, Tm, Yb, Lu, and U, and where 0<x<1. These glass ceramics have a low coefficient of thermal expansion (CTE), strong attenuation or blocking of ultraviolet (UV) radiation at wavelengths of less than about 250 nm and near infrared (NIR) radiation at wavelengths ranging from about 700 nm to about 2500 nm.

In some embodiments, the glass ceramics described herein are optically transparent in the visible (i.e., wavelengths from about 400 nm to about 700 nm) region of the spectrum. That is, the glass ceramic has a transmittance of greater than about 1% over a 1 mm path (expressed herein as “%/mm”) over at least one 50 nm-wide wavelength band of light in a range from about 400 nm to about 700 nm. In some embodiments, the glass ceramic has a transmittance of at least greater than about 10%/mm, in other embodiments, greater than about 50%/mm, in other embodiments, greater than about 75%/mm, in other embodiments, greater than about 80%/mm, and in still other embodiments, greater than about 90%/mm over at least one 50 nm-wide wavelength band of light in the visible region of the spectrum. In addition, these glass ceramics absorb light in the ultraviolet (UV) region (wavelengths of less than about 370 nm) and near infrared (NIR) region (from greater than about 700 nm to about 1700 nm) of the spectrum without use of coatings or films, which are mechanically fragile and sensitive to UV light and moisture. In some embodiments, the glass ceramic has a transmittance of less than 5%/mm and, in other embodiments, less than 1%/mm for light having a wavelength of about 370 nm or less. In some embodiments, the glass ceramic has an absorption of at least 90%/mm, in other embodiments, at least than 95%/mm, and in other embodiments, at least than 99%/mm for light having a wavelength of about 370 nm or less. In some embodiments, the glass ceramic has a transmittance of less than 10%/mm and, in other embodiments, less than 5%/mm over at least one 50 nm-wide wavelength band of light for light in the NIR region (i.e., from about 700 nm to about 2500 nm) of the spectrum. In some embodiments, the glass ceramic has an absorption of at least 90%/mm and, in other embodiments, at least 95%/mm over at least one 50 nm-wide wavelength band of light for light in the NIR region (i.e., from about 700 nm to about 2500 nm) of the spectrum.

In some embodiments, the glass ceramics described herein are capable of withstanding temperatures of at least about 300° C., or, in some embodiments, at least about 200° C., without impairing their optical or mechanical properties. In some embodiments, the transmittance of the glass ceramic between about 500 nm and about 2500 nm changes by less than 10%/mm when the glass ceramic is heated at temperatures in a range from about 200° C. to about 300° C. for periods of at least one hour. These glass ceramics are, in some embodiments, unreactive and otherwise impervious to oxygen, hydrogen, and moisture. The impervious nature of the glass ceramic has been demonstrated by exposing selected samples (e.g., samples 13, 14, 15, and 16 in Table 1) to 312 nm and 365 nm light for periods of up to 7 days. No change in the optical absorbance of these samples was observed following such exposure, indicating that oxygen, moisture, and/or hydrogen did not react with and alter the M_(x)WO₃ crystalline phase.

In some embodiments, the glass ceramics described herein have a coefficient of thermal expansion (CTE) at temperatures ranging from about 0° C. to about 300° C. of about 75×10⁻⁷° C.⁻¹. In some embodiments, the glass ceramics have a coefficient of thermal expansion (CTE) at temperatures ranging from about 0° C. to about 300° C. from about 33.5×10⁻⁷° C.⁻¹ to about 66.3×10⁻⁷° C.⁻¹ (e.g., samples 2, 11, 12, 13, and 54 in Table 1).

In some embodiments, the glass ceramics described herein are bleachable—i.e., the crystalline M_(x)WO₃ may be “erased” by thermally treating the glasses/glass ceramics for a short period above their respective softening points. Such thermal treatment may be performed using those energy sources known in the art, such as, but not limited to, resistance furnaces, lasers, microwaves, or the like. Composition 37 (Table 1), for example, may be bleached by holding the material at a temperature between about 685° C. and about 740° C. for approximately 5 minutes. The M_(x)WO₃ bronze phase may then be re-formed or re-crystallized on the surface of the material by exposure to a UV-pulsed laser; i.e., the tungsten bronze phase will be re-formed in those areas exposed to the laser.

The glass ceramics described herein may be used for low-emittance glazing in architectural, automotive, medical, aerospace, or other applications, including thermal face shields, medical eyewear, optical filters, and the like. In some embodiments, the glass ceramic forms a portion of a consumer electronic product, such as a cellular phone or smart phone, laptop computer, tablet, or the like. Such consumer electronic products typically comprise a housing having front, back, and side surfaces, and includes electrical components, which are at least partially internal to the housing. The electrical components include at least a power source, a controller, a memory, and a display. In some embodiments, the glass ceramic described herein comprises at least a portion of a protective element, such as, but not limited to, the housing and/or display.

In some embodiments, the glass phase is a borosilicate glass and the glass ceramic comprises SiO₂, Al₂O₃, B₂O₃, WO₃, and at least one alkali metal oxide R₂O, where R₂O is at least one of Na₂O, K₂O, Cs₂O, and/or Rb₂O, and the crystalline tungsten bronze phase is an tungsten bronze solid solution containing, comprising, or consisting essentially of MWO₃, where M is at least one of Na₂O, K₂O, Cs₂O, and Rb₂O. In some embodiments, the crystalline alkali tungsten bronze phase is a crystalline alkali tungsten bronze phase which is a mixture of alkali tungsten bronze solid solutions M1_(x)M2_(y)WO₃, where M1=Li, Na, K, Cs, Rb and M2=Li, Na, K, Cs, Rb, where M1≠M2 and 0<(x+y)<1.

In some embodiments, the glass ceramic comprises: from about 56 mol % to about 78 mol % SiO₂ (56 mol %≦SiO₂≦78 mol %) or from about 60 mol % to about 78 mol % SiO₂ (60 mol %≦SiO₂≦78 mol %); from about 8 mol % to about 27 mol % B₂O₃ (8 mol %≦B₂O₃≦27 mol %); from about 0.5 mol % to about 14 mol % Al₂O₃ (0.5 mol %≦Al₂O₃≦14 mol %); from greater than 0 mol % to about 10 mol % of at least one of Na₂O, K₂O, Cs₂O, and Rb₂O (0 mol %<Na₂O+K₂O+Cs₂O+Rb₂O≦9 mol %); from about 1 mol % to about 10 mol % WO₃ (1 mol %≦WO₃≦10 mol %) or, in some embodiments, from about 1 mol % to about 5 mol % WO₃ (1 mol %≦WO₃≦5 mol %); and from 0 mol % to about 0.5 SnO₂ (0 mol %≦SnO₂≦0.5). In some embodiments, the glass ceramic may comprise from 0 mol % to about 9 mol % Li₂O; in some embodiments, from 0 mol % to about 9 mol % Na₂O (0 mol %<Na₂O≦9 mol %); in some embodiments, from 0 mol % to about 9 mol % K₂O (0 mol %<K₂O≦9 mol %) or from 0 mol % to about 3 mol % K₂O (0 mol %<K₂O≦3 mol %); in some embodiments, from 0 mol % to about 10 mol % Cs₂O (0 mol %<Cs₂O≦10 mol %) or from greater than 0 mol % to about 7 mol % Cs₂O (0 mol %<Cs₂O≦7 mol %); and/or, in some embodiments, from 0 mol % to about 9 mol % Rb₂O (0 mol %<Rb₂O≦9 mol %). In some embodiments, the glass ceramic comprises from about 9.8 mol % to about 11.4 mol % B₂O₃ (9.8 mol %≦B₂O₃≦11.4 mol %).

In certain embodiments, the glass ceramics described herein comprise: from about 80 mol % to about 97 mol % SiO₂ (80 mol %≦SiO₂≦97 mol %); from 0 mol % to about 5 mol % Al₂O₃ (0 mol %≦Al₂O₃≦5 mol %); from 0 mol % to about 2 mol % R₂O (0 mol %≦R₂O≦2 mol %), where R₂O=Li₂O, Na₂O, K₂O, and/or Cs₂O, or from greater than 0 mol % to about 2 mol % Cs₂O (0 mol %<Cs₂O≦2 mol %), or from greater than 0 mol % to about 0.5 mol % Cs₂O (0 mol %<Cs₂O≦0.5 mol %); and from about 0.2 mol % to about 2 mol % WO₃ (0.2 mol %≦WO₃≦2 mol %). In particular embodiments, the glass ceramics comprise: from about 87 mol % to about 93 mol % SiO₂ (87 mol %≦SiO₂≦93 mol %); from 0 mol % to about 0.5 mol % Al₂O₃ (0 mol %≦Al₂O₃≦0.5 mol %); from 3 mol % to about 6 mol % B₂O₃ (3 mol %≦B₂O₃≦6 mol %); from 0.75 mol % WO₃ to about 1.25 mol % WO₃ (0.75 mol %≦WO₃≦1.25 mol %); and from 0.2 mol % to about 2 mol % R₂O, where R=Li, Na, K, and/or Cs (0.2 mol %≦R₂O≦2 mol %).

In some embodiments, the glass ceramic may further comprise at least one of: up to about 0.5 mol % MgO (0 mol %≦MgO≦0.5 mol %); up to about 2 mol % P₂O₅ (0 mol %≦P₂O₅≦2 mol %); and up to about 1 mol % (0 mol %≦ZnO≦1 mol %). The rate of formation of M_(x)WO₃ upon cooling or heat treatment may be increased by the addition of at least one of MgO (e.g., samples 55, 56, and 57 in Table 1), P₂O₅. (e.g., sample 58 in Table 1), and ZnO up (e.g., sample 59 in Table 1).

Non-limiting compositions of glass ceramics that are transparent in the visible light range and UV and NIR-absorbing are listed in Table 1. Compositions that do not absorb either UV or NIR radiation are listed in Table 2.

TABLE 1 Compositions of glass ceramics that are optically transparent in the visible light range and absorbing in the UV and NIR light ranges. Mol % 1 2 3 4 5 6 7 8 9 10 SiO₂ 76.9 75.9 72.9 69.9 65.9 77.6 76.9 61.7 61.7 65.9 B₂O₃ 17 17 20 23 27 20 17 20 20 20 Al₂O₃ 2 2 2 2 2 0.66 1.32 6.6 6.6 5 Li₂O 0 0 0 0 0 0 0 0 0 0 Na₂O 0 0 0 0 0 0 0 0 0 0 K₂O 0 0 0 0 0 0 0 0 0 0 Cs₂O 1 2 2 2 2 0.66 0.66 1.32 6.6 5 WO₃ 3 3 3 3 3 1 1 1 5 4 SnO₂ 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 La₂O₃ 0 0 0 0 0 0 0 0 0 0 Eu₂O₃ 0 0 0 0 0 0 0 0 0 0 MnO₂ 0 0 0 0 0 0 0 0 0 0 Fe₂O₃ 0 0 0 0 0 0 0 0 0 0 CeO₂ 0 0 0 0 0 0 0 0 0 0 Sb₂O₃ 0 0 0 0 0 0 0 0 0 0 MgO 0 0 0 0 0 0 0 0 0 0 Mol % 11 12 13 14 15 16 17 18 19 20 SiO₂ 64.9 63.9 63.9 63.9 63.9 63.9 62.9 61.9 64.9 62.9 B₂O₃ 20 20 20 20 20 20 20 20 20 20 Al₂O₃ 5 7 9 9 9 9 10 11 9 9 Li₂O 0 0 0 3 0 0 0 0 0 0 Na₂O 0 0 0 0 3 0 0 0 0 0 K₂O 0 0 0 0 0 3 0 0 0 0 Cs₂O 5 5 3 0 0 0 3 3 2 4 WO₃ 5 4 4 4 4 4 4 4 4 4 SnO₂ 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 La₂O₃ 0 0 0 0 0 0 0 0 0 0 Eu₂O₃ 0 0 0 0 0 0 0 0 0 0 MnO₂ 0 0 0 0 0 0 0 0 0 0 Fe₂O₃ 0 0 0 0 0 0 0 0 0 0 CeO₂ 0 0 0 0 0 0 0 0 0 0 Sb₂O₃ 0 0 0 0 0 0 0 0 0 0 MgO 0 0 0 0 0 0 0 0 0 0 Mol % 21 22 23 24 25 26 27 28 29 30 SiO₂ 63.9 61.9 63.9 63.9 63.9 64 64.4 64.9 65.4 64.9 B₂O₃ 20 20 20 20 20 20 20 20 20 20 Al₂O₃ 10 12 9 9 9 9 9 9 9 9 Li₂O 0 0 0 1.5 1.5 3 3 3 3 2 Na₂O 0 0 0 0 0 0 0 0 0 0 K₂O 0 0 0 1.5 0 0 0 0 0 0 Cs₂O 2 2 2.9 0 1.5 0 0 0 0 0 WO₃ 4 4 4 4 4 4 3.5 3 2.5 4 SnO₂ 0.1 0.1 0.1 0.1 0.1 0 0.1 0.1 0.1 0.1 La₂O₃ 0 0 0 0 0 0 0 0 0 0 Eu₂O₃ 0 0 0.1 0 0 0 0 0 0 0 MnO₂ 0 0 0 0 0 0 0 0 0 0 Fe₂O₃ 0 0 0 0 0 0 0 0 0 0 CeO₂ 0 0 0 0 0 0 0 0 0 0 Sb₂O₃ 0 0 0 0 0 0 0 0 0 0 MgO 0 0 0 0 0 0 0 0 0 0 Mol % 31 32 33 34 35 36 37 38 39 40 SiO₂ 65.9 66.9 65.9 66.4 60.9 65.9 69.9 66 65.9 65.8 B₂O₃ 20 20 20 20 20 15 10 20 20 20 Al₂O₃ 9 9 9 9 9 9 10 9 9 9 Li₂O 1 0 3 3 6 6 6 3 3 3 Na₂O 0 0 0 0 0 0 0 0 0 0 K₂O 0 0 0 0 0 0 0 0 0 0 Cs₂O 0 0 0 0 0 0 0 0 0 0 WO₃ 4 4 2 1.5 4 4 4 2 2 2 SnO₂ 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0 0.1 0.2 La₂O₃ 0 0 0 0 0 0 0 0 0 0 Eu₂O₃ 0 0 0 0 0 0 0 0 0 0 MnO₂ 0 0 0 0 0 0 0 0 0 0 Fe₂O₃ 0 0 0 0 0 0 0 0 0 0 MgO 0 0 0 0 0 0 0 0 0 0 Mol % 41 42 43 44 45 46 47 48 49 50 SiO₂ 65.6 65.8 65.9 70.1 70.1 69.85 70.35 70.1 69.9 68.1 B₂O₃ 20 20 20 10.35 9.8 9.8 9.8 12.35 10.35 11.35 Al₂O₃ 9 9 9 10 10 10 10 9 10 10 Li₂O 3 3 3 0 8.475 8.6 8.35 7.7 8.2 8.7 Na₂O 0 0 0 8.2 1.525 1.65 1.4 0.75 1.25 1.75 K₂O 0 0 0 1.25 0 0 0 0 0 0 Cs₂O 0 0 0 0 0 0 0 0 0 0 WO₃ 2 2 2 4 4 4 4 4 4 4 SnO₂ 0.4 0 0 0.1 0.1 0.1 0.1 0.1 0.3 0.1 La₂O₃ 0 0 0 0 0 0 0 0 0 0 Eu₂O₃ 0 0 0 0 0 0 0 0 0 0 MnO₂ 0 0.2 0 0 0 0 0 0 0 0 Fe₂O₃ 0 0 0.1 0 0 0 0 0 0 0 CeO₂ 0 0 0 0 0 0 0 0 0 0 Sb₂O₃ 0 0 0 0 0 0 0 0 0 0 MgO 0 0 0 0 0 0 0 0 0 0 Mol % 51 52 53 54 55 56 57 58 59 60 61 SiO₂ 69.85 69.85 69.85 69.85 70.25 69.85 69.35 68.85 69.1 69.75 68.75 B₂O₃ 9.8 9.8 9.8 9.8 9.8 9.8 9.8 9.8 9.8 9.8 10.8 Al₂O₃ 10 10 10 9.75 10 10 9.375 10 10 10 10 Li₂O 0 4 8 0 0 0 0 0 0 0 3 Na₂O 8.6 4.6 0.6 8.725 8.35 8.35 8.975 8.6 8.6 8.6 7.25 K₂O 1.65 1.65 1.65 1.775 1.4 1.4 1.4 1.65 1.65 1.65 0 Cs₂O 0 0 0 0 0 0 0 0 0 0 0 WO₃ 4 4 4 3.5 4 4 4 4 4 4 4 SnO₂ 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 La₂O₃ 0 0 0 0 0 0 0 0 0 0 0 Eu₂O₃ 0 0 0 0 0 0 0 0 0 0 0 MnO₂ 0 0 0 0 0 0 0 0 0 0 0 Fe₂O₃ 0 0 0 0 0 0 0 0 0 0 0 CeO₂ 0 0 0 0 0 0 0 0 0 0 0 Sb₂O₃ 0 0 0 0 0 0 0 0 0 0 0 MgO 0 0 0 0 0.1 0.5 1 0 0 0 0.1 P₂O₅ 0 0 0 0 0 0 0 0 0 0 0 ZnO 0 0 0 0 0 0 0 1 0 0 0 As₂O₅ 0 0 0 0 0 0 0 0 0.75 0 0

TABLE 2 Compositions of glass ceramics that do not absorb radiation in the UV and NIR light ranges. Mol % 62 63 64 65 66 67 68 69 70 71 SiO₂ 77.9 77.94 72.3 65.7 64.7 63.7 65.7 65.7 64.2 62.7 B₂O₃ 20.7 20 20 20 20 20 20 20 20 20 Al₂O₃ 0 0.3 3.3 6.6 6.6 0.66 5.6 4.6 8.1 9.6 Li₂O 0 0 0 0 0 0 0 0 0 0 Na₂O 0 0 0 0 0 0 0 0 0 0 K₂O 0 0 0 0 0 0 0 0 0 0 Cs₂O 0.3 0.66 3.3 6.6 6.6 6.6 7.6 8.6 6.6 6.6 WO₃ 1 1 1 1 2 3 1 1 1 1 SnO₂ 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 La₂O₃ 0 0 0 0 0 0 0 0 0 0 Eu₂O₃ 0 0 0 0 0 0 0 0 0 0 MnO₂ 0 0 0 0 0 0 0 0 0 0 Fe₂O₃ 0 0 0 0 0 0 0 0 0 0 CeO₂ 0 0 0 0 0 0 0 0 0 0 Sb₂O₃ 0 0 0 0 0 0 0 0 0 0 MgO 0 0 0 0 0 0 0 0 0 0 Mol % 72 73 74 75 76 77 78 79 80 81 SiO₂ 62.2 60.7 62.7 60.1 63.9 63.9 63.9 66.9 67.9 65.9 B₂O₃ 20 20 20 20 20 20 20 20 10 10 Al₂O₃ 8.1 9.6 6.6 6.6 5 9 9 9 10 10 Li₂O 0 0 0 0 0 0 0 3 8 10 Na₂O 0 0 0 0 0 0 0 0 0 0 K₂O 0 0 0 0 0 0 0 0 0 0 Cs₂O 6.6 6.6 6.6 6.6 7 0 0 0 0 0 WO₃ 3 3 4 6.6 4 4 4 1 4 4 SnO₂ 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 La₂O₃ 0 0 0 0 0 3 0 0 0 0 Eu₂O₃ 0 0 0 0 0 0 3 0 0 0 MnO₂ 0 0 0 0 0 0 0 0 0 0 Fe₂O₃ 0 0 0 0 0 0 0 0 0 0 CeO₂ 0 0 0 0 0 0 0 0 0 0 Sb₂O₃ 0 0 0 0 0 0 0 0 0 0 MgO 0 0 0 0 0 0 0 0 0 0 Mol % 82 83 84 85 86 87 88 89 90 79 SiO₂ 63.9 65.8 65.9 65.75 67 67 70.1 69.35 70.1 70.1 B₂O₃ 10 20 20 20 8.1 9.1 9.35 9.8 9.35 9.35 Al₂O₃ 10 9 9 9 12.6 12.6 10 10 10 10 Li₂O 12 3 3 3 5.1 5.1 8.242 8.35 8.7 8.7 Na₂O 0 0 0 0 6.2 5.7 2.208 1.4 1.75 1.75 K₂O 0 0 0 0 0.8 0.3 0 0 0 0 Cs₂O 0 0 0 0 0 0 0 0 0 0 WO₃ 4 2 2 2 4 4 4 4 2.5 2.5 SnO₂ 0.1 0 0 0 0.1 0.1 0.1 0.1 0.1 0.1 La₂O₃ 0 0 0 0 0 0 0 0 0 0 Eu₂O₃ 0 0 0 0 0 0 0 0 0 0 MnO₂ 0 0 0 0 0 0 0 0 0 0 Fe₂O₃ 0 0 0 0 0 0 0 0 0 0 CeO₂ 0 0.2 0 0.2 0 0 0 0 0 0 Sb₂O₃ 0 0 0.1 0.05 0 0 0 0 0 0 MgO 0 0 0 0 0 0 0 1 0 0

In some embodiments, −10 mol %≦R₂O (mol %)−Al₂O₃ (mol %)≦0.1 mol %. With respect to how composition and heat treatment affect the optical properties of the glass ceramic, peraluminous melts may be divided into three sub-categories. As used herein, the term “peraluminous melts” refer to melts in which the molar proportion or content of alumina that is greater than that of R₂O, where R₂O is at least one of Li₂O, Na₂O, K₂O, and Cs₂O; i.e. Al₂O₃ (mol %)>R₂O (mol %). The first sub-category is one in which peraluminous melts, when quenched rapidly from the molten state and after annealing, are transparent in the visible wavelength range and NIR regime (e.g., samples 12, 15-17, 20, 23, 25, 33, 35-42, 44, 46, 47, and 48 in Table 1). These materials require a subsequent heat treatment at or slightly above the anneal temperature but below the softening point in order to develop the NIR-absorbing nanocrystalline M_(x)WO₃ phase. The change in optical properties as a function of heat treatment is illustrated in FIG. 1, which is a plot of absorbance vs. wavelength for splat-quenched, annealed, and heat-treated samples of composition 13. As used herein, the term “splat-quenching” refers to the process of pouring a small amount or “glob” of molten glass onto an iron plate that is at room temperature and immediately pressing the glob with an iron plunger (also at room temperature) so as to rapidly cool the glass and press the glob into a thin (3-6 mm) disc of glass. While the splat-quenched (A in FIG. 1) and annealed samples (B) of composition/sample 13 show no absorption in the visible or NIR regimes, those samples that have been heat treated (C, D, E) exhibit absorbance in the NIR regime that increases with increasing heat treatment time, as well as some visible light attenuation at wavelengths in the 600-700 nm range, resulting in a material having a blue hue.

The second category of peraluminous melts remains transparent in the visible and NIR regimes if rapidly quenched, but exhibits NIR absorption post annealing (see samples 12, 14, 19, 21, 22, 24, and 26-32 in Table 1). As with the previously described group of peraluminous melts and shown in FIG. 2, which shows spectra of splat-quenched (A), annealed (B), and heat-treated (C) samples of glass ceramic composition 11, the NIR absorbance of the splat-quenched or annealed glass ceramic may be enhanced by further heat treatment.

The third category of peraluminous melts exhibits NIR absorption even upon rapid quenching (see samples 1 and 7 in Table 1). The NIR absorption of these materials may be further enhanced by subsequent heat treatment at or above the annealing point, but below the softening point.

Near-charge balanced melts (i.e., R₂O (mol %)−Al₂O₃ (mol %)=0±0.25 mol %) may, upon rapid quenching, be transparent in the visible and NIR absorbing post annealing (see samples 8-11 and 45 in Table 1), or NIR absorbing following either rapid quenching or annealing (see samples 2-7 in Table 1). As with the melts previously described hereinabove, NIR absorption may be further enhanced by subsequent heat treatment at or above the annealing point, but below the softening point.

Two peralkaline (i.e., R₂O (mol %)>Al₂O₃ (mol %)) UV- and NIR-absorbing melts (samples 46 and 50 in Table 1) were transparent in the visible and NIR when rapidly quenched but were NIR-absorbing after annealing. As with the melts previously described hereinabove, NIR absorption may be further enhanced by subsequent heat treatment at or above the annealing point, but below the softening point.

The rate of formation of the crystalline M_(x)WO₃ phase, which determines optical absorbance, may also be tuned by adjusting at least one of heat treatment time and temperature; the (R₂O (mol %)+Al₂O₃ (mol %))/WO₃ (mol %) ratio; the R₂O (mol %)/WO₃ (mol %) ratio; the Al₂O₃ (mol %)/WO₃ (mol %) ratio; and selection of alkali (or alkalis) to be batched. In all instances, more of the crystalline M_(x)WO₃ phase precipitates with longer heat treatment times, resulting in a material having stronger NIR absorption. However, excessive heat treatment times may cause the crystalline M_(x)WO₃ phase to coarsen. In some cases, coarsening may be accompanied by formation of a secondary or tertiary crystalline phase such as borastalite or aluminum borate. The formation of these secondary phases may produce a material that scatters visible wavelengths of light and thus appears hazy or opalescent. In addition, the rate of M_(x)WO₃ formation in most instances increases as the heat treatment temperature increases and approaches the softening point of the glass.

In some embodiments, 1≦(R₂O (mol %)+Al₂O₃ (mol %))/WO₃ (mol %)≦6. As the ratio (R₂O (mol %)+Al₂O₃ (mol %))/WO₃ (mol %) increases, the rate of M_(x)WO₃ formation decreases. When (R₂O (mol %)+Al₂O₃ (mol %))/WO₃ (mol %)≧6, the NIR-absorbing crystalline M_(x)WO₃ phase ceases to precipitate from the melt.

In those glasses in which the crystalline M_(x)WO₃ NIR-absorbing phase precipitates, the ratio R₂O (mol %)/WO₃ (mol %) is greater than or equal to 0 and less than or equal to about 4 (0≦R₂O (mol %)/WO₃ (mol %)≦4), and the ratio Al₂O₃ (mol %)/WO₃ (mol %) is in a range from about 0.66 and about 6 (0.66≦Al₂O₃ (mol %)/WO₃ (mol %)≦6). When R₂O (mol %)/WO₃ (mol %) is greater than 4 (R₂O (mol %)/WO₃ (mol %)>4), the glasses may precipitate a dense immiscible second phase and separate, resulting in an inhomogeneous melt. When the Al₂O₃ (mol %)/WO₃ (mol %) ratio exceeds 6 (Al₂O₃ (mol %)/WO₃ (mol %)>6), the glasses cease to precipitate the crystalline M_(x)WO₃ NIR-absorbing phase. When the Al₂O₃ (mol %)/WO₃ (mol %) ratio equals 6 (Al₂O₃ (mol %)/WO₃ (mol %)=6), such as in sample 34 in Table 1, the NIR absorbing nanocrystalline M_(x)WO₃ bronze forms, but does so very slowly. It is preferable that the R₂O (mol %)/WO₃ (mol %) ratio is in a range from about 0 to about 3.5 (0≦R₂O/WO₃≦3.5) (e.g., sample 26 in Table 1). Most preferably, R₂O/WO₃ is in a range from about 1.25 and about 3.5 (1.25≦R₂O (mol %)/WO₃ (mol %)≦3.5) (e.g., sample 53 in Table 1), as samples in this compositional range rapidly precipitate the UV and NIR absorbing M_(x)WO₃ crystalline phase, exhibit high visible transparency with strong NIR absorption, and are bleachable (i.e., the M_(x)WO₃ crystalline phase can be “erased”). The ratio Al₂O₃ (mol %)/WO₃ (mol %) is, in certain embodiments, is in a range from about 0.66 and about 4.5 (0.66≦Al₂O₃ (mol %)/WO₃ (mol %)≦4.5) (e.g., sample 40 in Table 1), and, most preferably, Al₂O₃ (mol %)/WO₃ (mol %) is is in a range from about 2 to about 3 (1≦Al₂O₃ (mol %)/WO₃ (mol %)≦3) (e.g., sample 61 in Table 1). Above this range, the NIR absorbing nanocrystalline M_(x)WO₃ bronze forms slowly.

Different alkali metal oxides cause the crystalline M_(x)WO₃ phase to precipitate at different rates. For melts having the same batched composition but with different alkali metal oxides R₂O (where R=Li, Na, K, or Cs) the M_(x)WO₃ precipitation rate is slowest when M (or R) is Cs, and fastest when M (or R) is Li—i.e., Cs<K<Na<Li (e.g., samples 14, 15, 16, and 13 in Table 1). The temperature at which the crystalline M_(x)WO₃ phase forms in the glass ceramic also shifts depending on the alkali metal that is present. FIG. 3 shows differential scanning calorimetry (DSC) cooling curves measured for samples 14, 15, 16, and 13, the compositions of which are listed Table 1. As seen in FIG. 3 and Table A below, the cesium-containing melt crystallizes at the highest temperature, followed by the potassium-containing, sodium-containing, and lithium-containing melts.

TABLE A Crystallization temperatures for crystalline M_(x)WO₃ phases. Crystallization Sample Alkali metal M Temperature (° C.) 14 Li 593.8 15 Na 682.2 16 K 706.3 13 Cs 714.1

The peak or maximum transmission wavelength in the visible range and NIR absorption edge of the glass ceramic may be tuned through composition, heat treatment time and temperature, and alkali metal oxide selection. Spectra of glass ceramics containing different alkali tungsten bronzes and otherwise having identical compositions (samples 14, 15, 16, and 13 in Table 1) are shown in FIG. 4. The potassium and cesium analogs (samples 16 and 13, respectively) and have shorter peak visible transmittance wavelengths (440-450 nm) than the sodium and lithium analogs (samples 15 and 14, respectively), which have peak visible transmittance wavelengths of 460 nm and 510 nm, respectively.

In some embodiments (e.g., examples 37, 44, 46, and 50 in Table 1), the glass ceramics described herein have a lower boron concentration—i.e., from about 9.8 mol % to about 11.4 mol % B₂O₃ (9.8 mol %≦B₂O₃≦11.4 mol %). In these samples, the NIR-absorbing crystalline M_(x)WO₃ phase is precipitated over a narrow and low temperature range, as shown in Table B. These compositions may be heated above their respective softening points and sagged, slumped, or formed, without growing the crystalline M_(x)WO₃ phase. This allows the optical performance of these glass ceramics to be controlled and tailored by first forming and/or shaping the glass article and then subsequently heat-treating the material at a low temperature to precipitate the NIR-absorbing crystalline M_(x)WO₃ second phase. In addition, the crystalline M_(x)WO₃ second phase in glass ceramics having the above compositions may be “erased” (and the glass ceramic “bleached”) by heating the glasses for a short period above their respective softening points. Composition 44, for example, can be bleached by holding the material at a temperature between about 685° C. and about 740° C. for approximately 5 minutes.

TABLE B Crystallization temperature ranges for crystalline M_(x)WO₃ phases in samples having low B₂O₃ content. Crystallization Temperature Sample B₂O₃ (mol %) Range (° C.) 37 10 575-625 44 10.4 500-550 46 9.8 500-575 50 11.4 500-650

In some embodiments, these glasses and glass ceramics may be patterned with UV lasers. The M_(x)WO₃ phase may be precipitated in rapidly quenched compositions (e.g., sample 14 in Table 1), for example, by exposing the material exposed to a 10 watt 355 nm pulsed laser.

Table C lists physical properties, including strain, anneal and softening points, coefficients of thermal expansion (CTE), density, refractive indices, Poisson's ratio, shear modulus, Young's modulus, liquidus (maximum crystallization) temperature, and the stress optical coefficient (SOC) measured for selected sample compositions listed in Table 1. In addition, x-ray powder diffraction (XRD) profiles of splat-quenched and heat-treated glass ceramic compositions were obtained for selected samples listed in Table 1. FIGS. 5 and 6 are representative XRD profiles obtained for splat-quenched and heat-treated materials, both having composition 14 in Table 1, respectively. These XRD profiles demonstrate that as-quenched materials (FIG. 5) are amorphous and do not contain a crystalline M_(x)WO₃ phase prior to heat treatment, and heat-treated glass materials contain a crystalline M_(x)WO₃ second phase.

TABLE C Physical properties measured for glass ceramics having compositions selected from Table 1. Properties 2 11 12 13 14 15 16 Strain Pt. (° C.) 495 450 461 505.8 512.1 497.4 497.3 Anneal Pt. (° C.) 557 498 513 566.1 563.1 552.2 553.7 Soft Pt. PPV (° C.) 963.1 850.9 837.9 952.4 CTE (×10⁻⁷/° C.) 33.5 53.2 48.6 37 Density (g/cm³) 2.335 2.612 2.569 2.516 2.427 2.402 2.392 Refractive Index 1.4944 1.4997  633 nm Refractive Index 1.4798 1.4835 1549 nm Properties 33 34 35 36 45 46 50 Strain Pt. (° C.) 515.1 471.2 485.2 523.9 486.8 483 471.3 Anneal Pt. (° C.) 568.9 514.3 530.8 573.1 540.8 536.7 521.2 Soft Pt. PPV 725.6 769.6 857.9 831.5 822.2 797.3 (° C.) CTE (×10⁻⁷/° C.) Density (g/cm³): 2.307 2.416 2.429 2.452 Refractive Index 633 nm Refractive Index 1549 inn Poisson's Ratio 0.228 0.23 0.226 0.217 Shear Modulus 3.47 3.48 3.65 3.95 Mpsi Young's 8.53 8.56 8.96 9.61 Modulus Mpsi Stress Optical 4.176 4.033 3.763 Coefficient nm/nm/MPa Maximum >1320 1160 1175 1290 1210 1210 1155 Crystallization Temp (° C.) Primary Phase Unknown Unknown Mullite Mullite Cassiterite Cassiterite Cassiterite Comments Devitrified Cassiterite Cassiterite to hot end up to up to 1155° C. 1170° C. Properties 51 52 53 54 Strain Pt. (° C.) 489.7 466.5 Anneal Pt. (° C.) 544.4 522.3 Soft Pt. PPV (° C.) CTE (×10⁻⁷/° C.) 64.4 57.3 Density (g/cm³): Refractive Index  633 nm Refractive Index 1549 nm Poisson's Ratio 0.219 0.219 0.219 0.214 Shear Modulus 0.217 3.79 3.88 3.55 Mpsi Young's Modulus 8.60 9.25 9.47 8.62 Mpsi Stress Optical 3.838 3.628 3.65 3.81 Coefficient nm/nm/MPa Maximum Crystallization Temp (° C.) Primary Phase Comments

In those embodiments in which the glass ceramic comprises alumina (Al₂O₃) and at least one alkali metal, the glass ceramic may be ion exchangeable. Ion exchange is commonly used to chemically strengthen glasses. In one particular example, alkali cations within a source of such cations (e.g., a molten salt, or “ion exchange,” bath) are exchanged with smaller alkali cations within the glass to achieve a layer under a compressive stress (CS) extending from the surface, where CS is the maximum, of the glass to a depth of layer (DOL) or depth of compression DOC within the glass phase. For example, potassium ions from the cation source are often exchanged with sodium ions within the glass phase.

In some embodiments, the glass ceramic is ion exchanged and has a compressive layer extending from at least one surface to a depth (as indicated by DOC and/or DOL) of at least about 10 μm within the glass ceramic. The compressive layer has a compressive stress CS of at least about 100 MPa and less than about 1500 MPa at the surface.

In non-limiting examples, compositions 51 and 54 were ion exchanged. The samples were first heat-treated at 550° C. for 15 hours, then cooled at 1° C./min to 475° C., and further cooled to room temperature at the rate of cooling of the furnace when power is shut off (furnace rate). The cerammed samples were then ion exchanged at 390° C. for 3 hours in a molten bath of KNO₃ resulting in surface compressive stresses of 360 MPa and 380 MPa and depths of layers of 31 and 34 microns for glass-ceramic compositions 51 and 54, respectively.

In one embodiment, the glass ceramics described herein may be made using a melt quench process. Appropriate ratios of the constituents may be mixed and blended by turbulent mixing or ball milling. The batched material is then melted at temperatures ranging from about 1550° C. to about 1650° C. and held at temperature for times ranging from about 6 to about 12 hours, after which time it may be cast or formed and then annealed. Depending on the composition of the material, additional heat treatments at or slightly above the annealing point, but below the softening point, to develop the crystalline M_(x)WO₃ second phase and provide UV- and NIR-absorbing properties. Optimal UV- and NIR-absorbing properties have been obtained with compositions of samples 12-16, 37, 46, 50-53 and 61 in Table 1. Heat-treatment times and temperature ranges used to develop the crystalline M_(x)WO₃ second phase for exemplary compositions are listed in Table D.

TABLE D Heat Treatment temperature and time ranges used to produce UV- and NIR- absorbing M_(x)WO₃ glass ceramics via the melt-quench process. Composition Heat Treatment Heat Treatment Time (Table 1) Temperature Range (° C.) Range (hours) 12 520-550 20-30 13 650-725 0.5-1.5 14 575-700 0.08-0.5 15 625-725 0.4-2 16 650-725 0.5-2 37 600-625 16-30 46 525-600 0.75-10 50 525-650 0.75-10 51 525-600 0.75-10 52 525-575 1-10 53 525-575 0.5-5 61 525-650 0.2-2

In other embodiments, the glass ceramic is formed by infiltrating a nano-porous glass such as, but not limited to, VYCOR®, a high-silica glass manufactured by Corning Incorporated. Such nano-porous glasses may be 20 to 30% porous with a 4.5-16.5 nm average pore diameter, with a narrow pore size distribution (with about 96% of the pores in the glass being +0.6 nm from the average diameter). The average pore diameter may be increased to about 16.5 nm by adjusting the heat treatment schedule required to phase separate the glass and by modifying etching conditions. A flow chart for the method of infiltrating a glass and forming the glass ceramic is shown in FIG. 7.

In step 110 of method 100, a first solution containing tungsten, a second solution containing the metal cation M, and a third solution of boric acid are prepared or provided to deliver these components to a nano-porous glass substrate. In one embodiment, the tungsten solution is prepared by dissolving ammonium metatungstate (AMT) in deionized water to produce a desired concentration of tungsten ions. In some embodiments, organic precursors, such as tungsten carbonyl, tungsten hexachloride, or the like may be used to deliver the tungsten into the pores of the nano-porous glass substrate. A number of aqueous precursors, including nitrates, sulfates, carbonates, chlorides, or the like may also be used to provide the metal M cation in the M_(x)WO₃ bronze.

In one non-limiting example, a first aqueous solution of 0.068 M AMT and a second aqueous solution 0.272 M of cesium nitrate are prepared or provided such that the cesium cation concentration is ⅓ of the tungsten cation concentration.

The third solution is a super-saturated boric acid solution which, in some embodiments, may be prepared by adding boric acid hydrate to deionized water, and heating the mixture to boiling while stirring.

In some embodiments (not shown in FIG. 7), the nano-porous glass may be cleaned prior to forming the glass ceramic. Samples (e.g., 1 mm sheets) of glass may first be slowly heated in ambient air to a temperature of about 550° C. to remove moisture and organic contaminants, and subsequently kept stored at about 150° C. until ready for use.

The nano-porous glass is first infiltrated with the tungsten solution (step 120) by immersing the glass in the first, tungsten-containing solution at room temperature (about 25° C.). In one non-limiting example, the nano-porous glass is immersed in the first solution for about one hour. The glass sample may then be removed from the first solution, soaked for about one minute in deionized water, and dried in ambient air for times ranging from about 24 to about 72 hours.

In the next step of method 100, the infiltrated nano-porous glass sample is heated in flowing oxygen to decompose the ammonium tungsten metatungstate and form WO₃ (step 130). The glass is first heated to about 225° C. at a rate of about 1° C./minute, then heated from about 225° C. to about 450° C. at a rate of 2.5° C./minute followed by a four hour hold at 450° C., and then cooled from about 450° C. to room temperature at a rate in a range from about 5° C. to about 7° C. per minute. Step 130 may, in some embodiments, include pre-heating the glass at about 80° C. for up to about 24 hours prior to the above heat treatment.

Following step 130, the glass is immersed in the second solution (step 140) at room temperature (about 25° C.) to infiltrate the glass with the M cation solution. Step 140 may, in some embodiments, be preceded by pre-heating the glass at about 80° C. for up to about 24 hours prior to immersion. In one non-limiting example, the nano-porous glass is immersed in the second solution for about one hour. The glass sample may then be removed from the second solution, soaked for about one minute in deionized water, and dried in ambient air for times ranging from about 24 to about 72 hours.

Following step 140, the nano-porous glass sample is heated to form the crystalline tungsten bronze M_(x)WO₃ phase (step 150). Heating step 150 includes first heating the glass from about 5° C. to about 200° C. at a rate (ramp rate) of about 1° C./minute in a nitrogen atmosphere, followed by heating from about 200° C. to about 575° C. at a rate of about 3° C./minute under an atmosphere of 3% hydrogen and 97% nitrogen and a one hour hold at 575° C., and then rapidly cooling the glass to about 300° C. by opening the furnace in which the heating step takes place. In some embodiments, the sample is then left to stand in ambient air for an unspecified time.

Following step 150, the glass sample is immersed in the third solution, which is a supersaturated boric acid solution (step 160). The third solution is maintained at boiling and gently stirred during step 160. In some embodiments, the glass sample is immersed in the boiling solution for about 30 minutes. After removal from the third solution the sample, in some embodiments, is washed with deionized water and left to stand in ambient air for about 24 hours. The glass is then heated under a nitrogen atmosphere to form and consolidate the glass ceramic (step 170). The glass is first heated from room temperature to about 225° C. at a ramp rate of about 1° C./minute in step 170, followed by heating from about 225° C. to about 800° C. at a rate of about 5° C./minute. The glass is held at 800° C. for about one hour and then cooled from about 800° C. to room temperature at a rate of about 10° C./minute.

In another aspect, glasses doped with rare earth oxides (REO) and having high absorbance in the NIR region of the spectrum are provided. In some embodiments, these REO-doped glasses contribute to high refractive index of the glass in the infrared (IR). The rare earth oxide dopants, which include Sm₂O₃, Pr₂O₃, and Er₂O₃, comprise up to about 30 mol % of the glass.

In some embodiments, the REO-doped glasses are aluminosilicate glasses comprising Al₂O₃ and SiO₂ and at least one of Sm₂O₃, Pr₂O₃, and Er₂O₃, where Sm₂O₃+Pr₂O₃+Er₂O₃≦30 mol %, in some embodiments, Sm₂O₃+Pr₂O₃+Er₂O₃≦28 mol % and, in other embodiments, Sm₂O₃+Pr₂O₃+Er₂O₃≦25 mol %. In some embodiments, these REO-doped glasses may comprise up to about 30 mol % Pr₂O₃ or up to about 25 mol % Pr₂O₃. In other embodiments, these REO-doped glasses may comprise up to 28 mol % Sm₂O₃ or up to 26 mol % Sm₂O₃. The REO-doped aluminosilicate glasses may comprise from about 40 mol % to about 72 mol % SiO₂ (40 mol %≦SiO₂≦72 mol %) or from about 50 mol % to about 72 mol % SiO₂ (50 mol %≦SiO₂≦72 mol %) and from about 8 mol % to about 45 mol % Al₂O₃ (8 mol %≦Al₂O₃≦45 mol %), or from about 8 mol % to about 20 mol % Al₂O₃ (8 mol %≦Al₂O₃≦20 mol %) or from about 8 mol % to about 18 mol % Al₂O₃ (8 mol %≦Al₂O₃≦18 mol %). In some embodiments, the glasses further comprise at least one alkaline earth oxide and/or B₂O₃, where 0 mol %≦MgO+CaO+BaO≦24 mol % and 0 mol %≦B₂O₃≦6 mol %. The glasses, in some embodiments, have less than about 30% transmission at a wavelength between about 1400 nm and about 1600 nm. Non-limiting examples of compositions of aluminosilicate glasses are listed in Table E. Refractive indices (RI) measured for these glasses are also listed in Table E. Glasses A, B and C, which contain no alkaline earth modifiers, were found to be too viscous to pour, even at 1650° C. Glasses E and F, which contain appreciable amounts (>21 mol %) of alkaline earth modifiers, as well as B₂O₃ are pourable at 1650° C. Dispersion and percent transmittance for Glass E for both the visible and NIR regions of the spectrum are plotted in FIGS. 8 and 9, respectively. Glass E exhibits both a high refractive index in the infrared (IR) region and high absorbance at 1550 nm. UV-VIS-IR spectra of these compositions containing 3-5 mol %% Pr₂O₃ are plotted in FIG. 10, and show the high absorbance of these glasses at 1550 nm.

TABLE E Compositions and refractive indices of rare earth-doped aluminosilicate glasses. Mol % A B C D E F MgO 0 0 0 9.2 8.8 8.8 CaO 0 0 0 9.2 8.8 8.8 BaO 0 6 6 3.4 3.2 3.2 Al₂O₃ 18 18 18 10.7 10.2 10.2 B₂O₃ 0 0 0 4.6 4.4 4.4 SiO₂ 70 70 70 62.9 59.9 59.9 Pr₂O₃ 12 6 0 0 4.8 0.0 Sm₂O₃ 0 0 6 0 0 4.8 RI at 1.604 1.565 1.562 1.528 1.58 1.576 1550 nm Mol % E-1 E-2 E-3 E-4 MgO 8.4 8.0 7.7 7.4 CaO 8.4 8.0 7.7 7.4 BaO 3.1 3.0 2.8 2.7 Al₂O₃ 9.7 9.3 8.9 8.6 B₂O₃ 4.2 4.0 3.8 3.7 SiO₂ 57.2 54.7  52.4  50.3 Pr₂O₃ 9.1 13.0  16.7  20.0 Sm₂O₃ 0 0   0   0 Mol % DP DQ DR DT DU DW EC Pr₂O₃ 0 0 0 0 0 0 0 Sm₂O₃ 20 22 18 22 18 22 0 Er₂O₃ 0 0 0 0 0 0 20 Al₂O₃ 16 18 22 22 26 26 18 SiO₂ 64 60 60 56 56 52 62 Mol % ED ES FA FB FC FD FE Pr₂O₃ 0 0 20 20 20 26 28 Sm₂O₃ 0 26 0 0 0 0 0 Er₂O₃ 22 0 0 0 0 0 0 Al₂O₃ 24 22 20 30 40 20 28 SiO₂ 54 52 60 50 40 54 44

In some embodiments, the REO-doped glasses are zinc-bismuth-borate glasses comprising ZnO, Bi₂O₃, B₂O₃, and at least one of Sm₂O₃, Pr₂O₃, and Er₂O₃, where Sm₂O₃+Pr₂O₃+Er₂O₃≦10 mol % or, in other embodiments, Sm₂O₃+Pr₂O₃+Er₂O₃≦5 mol %. In some embodiments, these REO-doped glasses may comprise up to about 10 mol % Pr₂O₃. In other embodiments, these REO-doped glasses may comprise up to 10 mol % Sm₂O₃. The REO-doped Zn—Bi-borate glasses may comprise from about 20 mol % to about 30 mol % ZnO (20 mol %≦ZnO≦30 mol %), from about 4 mol % to about 20 mol % Bi₂O₃ (4 mol %≦Bi₂O₃≦20 mol %), and from about 40 mol % to about 50 mol % B₂O₃ (40 mol %≦B₂O₃≦50 mol %). In some embodiments, the REO-doped Zn—Bi-borate glasses further comprise at least one of Na₂O and TeO₂, where 0 mol %≦TeO₂≦6 mol % and 0 mol %≦Na₂O≦15 mol %. The glasses, in some embodiments, have less than about 30% transmission at a wavelength between about 1400 nm and about 1600 nm. Non-limiting examples of compositions of Zn—Bi-borate glasses are listed in Table F. Refractive indices (RI) measured for these glasses are also listed in Table F.

TABLE F Compositions of rare earth-doped Zn—Bi-borate glasses. Mol % G H I J K L ZnO 26.2 26.2 28.5 21.7 21.2 25.7 Bi₂O₃ 4.9 4.9 19 14.6 14.3 4.8 B₂O₃ 43.6 43.6 47.5 41.5 40.7 42.9 TeO₂ 5.8 5.8 0 0.0 0.0 5.7 Na₂O 14.1 14.1 0 9.7 9.5 13.8 BaO 2.4 2.4 0 9.7 9.5 2.4 Pr₂O₃ 3 0 5 2.9 4.8 4.8 Sm₂O₃ 0 3 0 0 0.0 0.0 RI at 1.683 1.680 1.857 not. not. not. 1550 nm measured measured measured

In other embodiments, the REO-doped glasses described herein are phosphate or aluminophosphate glasses. Rare earth metaphosphates having a molar ratio 25Ln₂O₃:75P₂O₅, where Ln represents the rare earth elements, form glasses having reasonable durability. Durability may be further improved by including Al₂O₃ in the glass. REO-doped aluminophosphate glasses, in some embodiments, may comprise from about 6 mol % to about 25% Ln₂O₃ (6 mol %≦Ln₂O₃≦22.5 mol %), where Ln=Sm₂O₃+Pr₂O₃+Er₂O₃, from about 5 mol % to about 27% Al₂O₃ (5 mol %≦Al₂O₃≦27 mol %), and from about 67 mol % to about 74 mol % P₂O₅ (67 mol %≦P₂O₅≦67 mol %). In certain embodiments, such glasses comprise from about 6 mol % to about 22.5% Sm₂O₃ (6 mol %≦Sm₂O₃≦22.5 mol %), from about 5 mol % to about 27% Al₂O₃ (5 mol %≦Al₂O₃≦27 mol %), and from about 67 mol % to about 74 mol % P₂O₅ (67 mol %≦P₂O₅≦67 mol %). Non-limiting examples of compositions of samarium-doped aluminophosphate glasses are listed in Table G.

TABLE G Compositions of rare earth-doped aluminophosphate glasses. Mol % M N O P Q R S Sm₂O₃ 21 17 20 13.5 10 13 6 Al₂O₃ 5 10 10 15 20 20 25 P₂O₅ 74 73 70 71.5 70 67 69

While typical embodiments have been set forth for the purpose of illustration, the foregoing description should not be deemed to be a limitation on the scope of the disclosure or appended claims. Accordingly, various modifications, adaptations, and alternatives may occur to one skilled in the art without departing from the spirit and scope of the present disclosure or appended claims. 

1. A glass ceramic, the glass ceramic comprising a silicate glass phase; and from about 0.1 mol % to about 10 mol % of a crystalline M_(x)WO₃ phase comprising nanoparticles, where M is at least one of H, Li, Na, K, Rb, Cs, Ca, Sr, Ba, Zn, Cu, Ag, Sn, Cd, In, Tl, Pb, Bi, Th, La, Pr, Nd, Sm, Eu, Gd, Dy, Ho, Er, Tm, Yb, Lu, and U, and 0<x<1.
 2. The glass ceramic of claim 1, wherein the glass ceramic has a transmittance of at least 10%/mm over a wavelength band over at least one 50 nm-wide wavelength band of light for light having a wavelength in a range from about 400 nm to about 700 nm.
 3. The glass ceramic of claim 1, wherein the glass ceramic has transmittance of less than 1%/mm for light having a wavelength of about 370 nm or less.
 4. The glass ceramic of claim 1, wherein the glass ceramic has a transmittance of less than 5%/mm over at least one 50 nm-wide wavelength band of light for light having a wavelength in a range from about 700 nm to about 2500 nm.
 5. The glass ceramic of claim 4, wherein the transmittance of the glass ceramic between about 500 nm and about 2500 nm changes by less than 10%/mm when the glass ceramic is heated at a temperature in a range from about 200° C. to about 300° C.
 6. The glass ceramic of claim 1, wherein the glass ceramic is ion exchangeable.
 7. The glass ceramic of claim 6, wherein the glass ceramic is ion exchanged and has a compressive layer extending from a surface of the glass ceramic to a depth of at least about 10 μm within the glass ceramic, the compressive layer having a compressive stress of at least about 100 MPa and less than about 1500 MPa at the surface.
 8. The glass ceramic of claim 1, wherein the glass ceramic is bleachable by thermal treatment.
 9. The glass ceramic of claim 1, wherein the glass ceramic has a coefficient of thermal expansion of less than or equal to about 75×10⁻⁷° C.⁻¹ at temperatures ranging from 0° C. to about 300° C.
 10. The glass ceramic of claim 1, wherein the silicate glass phase is a borosilicate glass phase.
 11. The glass ceramic of claim 1, wherein the glass ceramic comprises from about 0.1 mol % to about 5 mol % of the crystalline M_(x)WO₃ phase.
 12. The glass ceramic of claim 1, wherein M is at least one alkali metal.
 13. The glass ceramic of claim 12, wherein the glass ceramic comprises: from about 56 mol % to about 78 mol % SiO₂; from about 8 mol % to about 27 mol % B₂O₃; from about 0.5 mol % to about 14 mol % Al₂O₃; from greater than 0 mol % to about 10 mol % of at least one of Na₂O, K₂O, Cs₂O, and Rb₂O; from about 1 mol % to about 10 mol % WO₃; and from 0 mol % to about 0.5 SnO₂.
 14. The glass ceramic of claim 12, wherein M is Cs and wherein the glass ceramic comprises from greater than 0 mol % to about 10 mol % Cs₂O.
 15. The glass ceramic of claim 12, wherein −10 mol %≦R₂O (mol %)−Al₂O₃ (mol %)≦0.1 mol %, where R₂O is at least one of Na₂O, K₂O, Cs₂O, and Rb₂O.
 16. The glass ceramic of claim 12, wherein 0<R₂O (mol %)/WO₃ (mol %)≦2.61, where R₂O is at least one of Na₂O, K₂O, Cs₂O, and Rb₂O.
 17. The glass ceramic of claim 12, wherein 0.66≦Al₂O₃ (mol %)/WO₃ (mol %)≦6.
 18. The glass ceramic of claim 12, wherein 1≦(R₂O (mol %)+Al₂O₃ (mol %))/WO₃ (mol %)≦6, where R₂O is at least one of Na₂O, K₂O, Cs₂O, and Rb₂O.
 19. The glass ceramic of claim 12, wherein the glass ceramic further comprises at least one of: up to about 0.5 mol % MgO; up to about 2 mol % P₂O₅; and up to about 1 mol %.
 20. The glass ceramic of claim 1, wherein the glass ceramic comprises: from about 80 mol % to about 97 mol % SiO₂; from 0 mol % to about 5 mol % Al₂O₃; from greater than 0 mol % to about 2 mol % Cs₂O; and from about 0.2 mol % to about 2 mol % WO₃.
 21. The glass ceramic of claim 1, wherein the crystalline M_(x)WO₃ phase comprises at least one of a plurality of platelet-shaped M_(x)WO₃ nanoparticles and a plurality of M_(x)WO₃ nanorods.
 22. The glass ceramic of claim 21, wherein the plurality of platelet-shaped M_(x)WO₃ nanoparticles has an average diameter in a range from about 10 nm to 5 m.
 23. The glass ceramic of claim 21, wherein the plurality of M_(x)WO₃ nanorods has an average length in a range from about 10 nm to about 1000 nm and an average width ranging in a range from about 2 nm to about 75 nm.
 24. The glass ceramic of claim 23, wherein the plurality of M_(x)WO₃ nanorods has an average length in a range from about 10 nm to about 200 nm and an average width ranging in a range from about 2 nm to about 30 nm.
 25. The glass ceramic of claim 1, wherein the glass ceramic is at least a portion of a thermal shield, an optical filter, an architectural element, an automotive component, or a housing for an electronic display.
 26. A glass ceramic, the glass ceramic comprising a silicate glass phase; and from about 0.1 mol % to about 10 mol % of a crystalline M_(x)WO₃ phase comprising nanoparticles, where M is at least one alkali metal, and 0<x<1.
 27. The glass ceramic of claim 26, wherein the glass ceramic comprises from about 0.1 mol % to about 5 mol % of the crystalline M_(x)WO₃ phase.
 28. The glass ceramic of claim 26, wherein the silicate glass phase is a borosilicate glass phase.
 29. The glass ceramic of claim 26, wherein the glass ceramic comprises: from about 56 mol % to about 78 mol % SiO₂; from about 9 mol % to about 27 mol % B₂O₃; from about 0.5 mol % to about 14 mol % Al₂O₃; from greater than 0 mol % to about 9 mol % of at least one of Na₂O, K₂O, Cs₂O, and Rb₂O; from about 1 mol % to about 10 mol % WO₃; and from 0 mol % to about 0.5 SnO₂.
 30. The glass ceramic of claim 26, wherein M is Cs and wherein the glass ceramic comprises from greater than 0 mol % to about 10 mol % Cs₂O.
 31. The glass ceramic of claim 26, wherein −10 mol %≦R₂O (mol %)−Al₂O₃ (mol %)≦0.1 mol %, where R₂O is at least one of Na₂O, K₂O, Cs₂O, and Rb₂O.
 32. The glass ceramic of claim 26, wherein 0<R₂O (mol %)/WO₃ (mol %)≦2.61, where R₂O is at least one of Na₂O, K₂O, Cs₂O, and Rb₂O.
 33. The glass ceramic of claim 26, wherein 0.66≦Al₂O₃ (mol %)/WO₃ (mol %)≦6.
 34. The glass ceramic of claim 26, wherein the glass ceramic further comprises at least one of: up to about 0.5 mol % MgO; up to about 2 mol % P₂O₅; and up to about 1 mol %.
 35. The glass ceramic of claim 26, wherein the glass ceramic has a transmission of at least 1%/mm over a wavelength band over at least one 50 nm-wide wavelength band of light for light having a wavelength in a range from about 400 nm to about 700 nm.
 36. The glass ceramic of claim 26, wherein the glass ceramic has a transmittance of less than 1%/mm for light having a wavelength of about 370 nm or less.
 37. The glass ceramic of claim 26, wherein the glass ceramic has a transmittance of less than 5%/mm over at least one 50 nm-wide wavelength band of light for light having a wavelength in a range from about 700 nm to about 2500 nm.
 38. The glass ceramic of claim 37, wherein the transmittance of the glass ceramic between about 500 nm and about 2500 nm changes by less than 10%/mm when the glass ceramic is heated at a temperature in a range from about 200° C. to about 300° C.
 39. The glass ceramic of claim 26, wherein the glass ceramic is ion exchangeable.
 40. The glass ceramic of claim 39, wherein the glass ceramic is ion exchanged and has a compressive layer extending from a surface of the glass ceramic to a depth of at least about 10 μm within the glass ceramic, the compressive layer having a maximum compressive stress of at least about 100 MPa and less than about 1500 MPa at the surface.
 41. The glass ceramic of claim 26, wherein the glass ceramic is bleachable by thermal treatment.
 42. The glass ceramic of claim 26, wherein the glass ceramic is impervious to moisture and oxygen.
 43. The glass ceramic of claim 26, wherein M includes Cs and the glass ceramic comprises: from about 80 mol % to about 97 mol % SiO₂; from 0 mol % to about 5 mol % Al₂O₃; from greater than 0 mol % to about 2 mol % Cs₂O; and from about 0.2 mol % to about 2 mol % WO₃.
 44. The glass ceramic of claim 26, wherein the crystalline M_(x)WO₃ phase comprises at least one of a plurality of platelet-shaped M_(x)WO₃ nanoparticles and a plurality of M_(x)WO₃ nanorods.
 45. The glass ceramic of claim 44, wherein the plurality of platelet-shaped M_(x)WO₃ nanoparticles has an average diameter in a range from about 10 nm to 5 m.
 46. The glass ceramic of claim 44, wherein the plurality of M_(x)WO₃ nanorods has an average length in a range from about 10 nm to about 1000 nm and an average width ranging in a range from about 2 nm to about 75 nm.
 47. The glass ceramic of claim 46, wherein the plurality of M_(x)WO₃ nanorods has an average length in a range from about 10 nm to about 200 nm and an average width ranging in a range from about 2 nm to about 30 nm.
 48. The glass ceramic of claim 26, wherein the glass ceramic is at least a portion of a thermal shield, an optical filter, an architectural element, an automotive component, or a protective element for an electronic display.
 49. An aluminosilicate glasses comprising from about 8 mol % to about 45 mol % Al₂O₃, from about 40 mol % to about 72 mol % SiO₂ and at least one of Sm₂O₃, Pr₂O₃, and Er₂O₃, wherein Sm₂O₃+Pr₂O₃+Er₂O₃≦30 mol %.
 50. The aluminosilicate glass of claim 49, further comprising at least one alkaline earth oxide and B₂O₃, wherein 0 mol %≦MgO+CaO+BaO≦24 mol % and 0 mol %≦B₂O₃≦6 mol %.
 51. The aluminosilicate glass of claim 49, wherein the glass comprises up to about 30 mol % Pr₂O₃.
 52. The aluminosilicate glass of claim 49, wherein the glass comprises up to about 28 mol % Sm₂O₃.
 53. The aluminosilicate glass of claim 49, wherein the aluminosilicate glass has less than about 30% transmission at a wavelength between about 1400 nm and about 1600 nm.
 54. A zinc-bismuth-borate glass comprising from about 20 mol % to about 30 mol % ZnO, from about 4 mol % to about 20 mol % Bi₂O₃, from about 40 mol % to about 50 mol % B₂O₃, and at least one of Sm₂O₃, Pr₂O₃, and Er₂O₃, wherein Sm₂O₃+Pr₂O₃+Er₂O₃≦10 mol %.
 55. The zinc-bismuth-borate glass of claim 54, further comprising at least one of Na₂O and TeO₂, wherein 0 mol %≦TeO₂≦6 mol % and 0 mol %≦Na₂O≦15 mol %.
 56. The zinc-bismuth-borate glass of claim 54, wherein the glass comprises up to about 10 mol % Pr₂O₃.
 57. The zinc-bismuth-borate glass of claim 54, wherein the glass comprises up to about 10 mol % Sm₂O₃.
 58. The zinc-bismuth-borate glass of claim 54, wherein the zinc-bismuth-borate glass has less than about 30% transmission at a wavelength between about 1400 nm and about 1600 nm.
 59. A phosphate glass comprising at least one rare earth oxide Ln₂O₃ and having a molar ratio 25Ln₂O₃:75P₂O₅, where Ln₂O₃ comprises at least one of Sm₂O₃, Pr₂O₃, and Er₂O₃.
 60. The phosphate glass of claim 59, wherein the phosphate glass comprises: from about 6 mol % to about 25% Ln₂O₃; from about 5 mol % to about 27% Al₂O₃; and from about 67 mol % to about 74 mol % P₂O₅.
 61. The phosphate glass of claim 59, wherein the phosphate glass comprises: from about 6 mol % to about 22.5% Sm₂O₃; from about 5 mol % to about 27% Al₂O₃; and from about 67 mol % to about 74 mol % P₂O₅. 